The instantaneous mechanical properties of room temperature and high temperature of 00Crl6Ni65Mol6Ti ( hastelloy C-276 alloy) in different states are shown in Table 8-37~Table 8-39. From these data, it is known that the plasticity of this alloy does not decrease even after aging. The plasticity of the as-welded state is reduced, but its application in engineering is still satisfactory. Since the alloy has good thermal stability, the precipitation after aging is much less than that of 00Cr16Ni60Mol6W4 alloy, so there is no significant difference in the solid solution state and the aging state plasticity, as shown in Figure 8-30.

Table 8-37 Performance of hastelloy C-276 (00Crl6Ni65Mol6Ti) alloy sheet

sheet thicknes /mm	Test status	Test temperature/℃	Rm/MPa	Rm/MPa	A/%	HB
1.6	1066℃ solid solution	room temperature	77.58	416. 56	52	90
		204	705. 57	402. 96	49
		316	674. 53	376. 65	52
		427	652. 40	319. 69	64

3. 1	1066℃ solid solution	room temperature	800. 62	420. 29	54	92
		204	677. 18	319.70	54
		316	671.77	302.47	59
		427	643.5	302. 47	62
		538	643.7	302. 40	55
		649	570. 50	290.70	50
		760	475.41	259. 75	44
3.9	1066℃ solid solution	room temperature	782.0	365. 17	55	91
		204	688. 30	274. 90	55
		316	649.70	248.72	61
		427	655. 22	249.4	68

Table 8-38 Properties of Hastelloy C-4 Alloy Sheet and Medium Plate Aging State

thickness/mm	test state	test temperature/℃	Rm/MPa	Rp0.2/MPa	A/%
3. 1	900℃ aging 100h	room temperature	789.60	376.20	56
		204	711.00	324. 50	54
		316	685. 55	296. 95	57
		427	658. 33	279. 70	60
		538	642. 80	274. 90	57
		649	596. 67	256. 30	56
		760	525. 00	250.00	56
9. 37	900℃ aging 100h	room temperature	770. 30	335.50	62
		204	693. 13	272. 15	51
		316	675. 22	254.9	56
		427	669. 70	254.9	57
		538	617.34	221. 16	53
		649	617.34	234.90	56
		760	506.40	204.60	70

Table 8-39 Properties of plates and weldments in H astelloy C-4 alloy

Medium plate and weldment thickness/mm	test condition	test temperature/℃	Rm/MPa	Rm/MPa	A/%
6.25	1066℃ Quench after solid solution	room temperature	766. 86	336. 20	58
		204	716.56	294. 89	54
		316	711.74	281. 10	55
		427	682. 11	254. 93	60

9.3	1066℃ Quench after solid solution		room temperature	790. 30	355. 50	59
			204	726. 20	300. 40	56
			316	703. 50	269. 40	59
			427	656. 60	257. 68	62
			538	642. 84	227. 37	52
			649	683. 58	213.59	52
			760	482. 30	210. 80	53
12.5	1066℃ Quench after solid solution		room temperature	804. 70	334. 85	63
			93			70
			204	763. 40	301. 10	61
			316	724. 82	263. 88	65
			427	706. 22	246. 66	66
			649	634. 56	235.64	71
Weldment 12. 5	TIC		room temperature	776. 50	470. 58	40
			260	653. 86	351.40	39
			538	601.50	342. 40	35
Weldment 12. 5	650℃ aging	10h	room temperature	783. 40	428.56	48
Weldment 12. 5	650℃ aging	1000h	room temperature	817. 84	410.64	46
Full weld	TIG		room temperature	737. 90	491.94	42